Molecular Formula | Li2O3Si |
Molar Mass | 89.97 |
Density | 2,52 g/cm3 |
Melting Point | 1204°C |
Water Solubility | insoluble cold H2O, decomposes in boiling H2O [MER06] |
Appearance | Powder |
Specific Gravity | 2.52 |
Color | white |
Sensitive | 2: reacts with aqueous acid |
Physical and Chemical Properties | Character odorless, tasteless transparent liquid. The relative density of 1.16~1.19(25 ℃) soluble in water and alkaline solution, insoluble alcohol and organic solvents. |
Use | Used in glass system, molten salt system and high temperature ceramic glaze, also used as steel and other surface anti-rust coatings |
Risk Codes | 36/37/38 - Irritating to eyes, respiratory system and skin. |
Safety Description | S26 - In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. S36/37/39 - Wear suitable protective clothing, gloves and eye/face protection. |
TSCA | Yes |
Raw Materials | Sodium silicate Sulfuric acid Lithium hydroxide |
odorless, tasteless transparent liquid. It is weakly alkaline, and the pH value is about 11. The relative density and viscosity of the product vary with the product type, and the relative density is between 1. 16 and 1. 19 (25 ℃). Soluble in water and alkaline solution, insoluble in alcohol and organic solvents. And acid free gel. It is self-drying, and after the evaporation of the water in the solution, a water-insoluble dry film can be formed, which has water irreversibility.
lithium hydroxide method: Sodium silicate is reacted with sulfuric acid to generate hydrated silicic acid and sodium sulfate, and the hydrated silicic acid is reacted with lithium hydroxide to generate lithium silicate and water to obtain lithium silicate product.
used as a binder, mainly for inorganic zinc-rich coating and advanced electrode.
This product is non-toxic and non-flammable. The use of iron or polyethylene plastic drum packaging. 25kg per barrel. Should be stored in a cool and ventilated warehouse, to avoid exposure to the sun during transport, to prevent freezing in winter, the requirements of 20~40 deg C under the conditions of storage and transportation.
EPA chemical substance information | information provided by: ofmpeb.epa.gov (external link) |
Application | used in glass system, molten salt system and high temperature ceramic glaze, also used for steel and other surface anti-rust coating used as a binder, mainly used for inorganic zinc-rich coatings and advanced electrode. |
production method | The lithium hydroxide method reacts sodium silicate with sulfuric acid to generate hydrated silicic acid and sodium sulfate, the hydrated silicic acid reacts with lithium hydroxide to generate lithium silicate and water to obtain lithium silicate product. |